Composition Variations and UV Irradiation Effect on Charge Transfer in PbMoO4 Single Crystals
(Oles Honchar Dnipro National University, 2022) Bochkova, Tatiana; Trubitsyn, Mykhailo P.; Volnianskii, M. D.; Volnyanskii, Dmytro M.
ENG: The effect of nonstoichiometry of the composition, PbO polymorphism, and preliminary irradiation with ultraviolet light on electrical conductivity of alternating current (AC) was studied in PbMoO4 crystals. The crystals were grown by Czochralski method in a direction deviated by 30° from a-axis in (001) plain. The charge was prepared from MoO3 and PbO, lead oxide was used of α- or β- structural modifications. The reagents were taken both in a stoichiometric ratio and with an excess of 0.5 mol % of MoO3. It was shown that the magnitude of the dark and irradiation-induced AC conductivity was affected both by the type of polymorphic form of PbO and by the excess amount of MoO3. The influence of the PbMoO4 crystal structural disorder on charge transfer processes are discussed within the framework of the model of hopping conduction in disordered media.
Effect of Lattice Disorder on Charge Transfer in Lead Molybdate Crystals
(Oles Honchar Dnipro National University, Ukraine, 2023) Bochkova, Tatiana; Krivchenko, A. Yu.; Trubitsyn, M. P.; Volnianskii, M. D.; Volnyanskii, Dmytro M.
ENG: Electrical properties of PbMoO4 crystals, grown from the stoichiometric charge and non- stoichiometric charge with an excess of MoO3, are studied and compared in this work. The crystals are grown by Czochralski method in the direction at an angle of 30° to [100] axis in (001) plane. The single crystals are free from gas bubbles, cracks and have a weak yellowish color. It is found that the addition of MoO3 excess (0.5 mol.%) to the stoichiometric charge notably increases the crystal lattice disorder. It is assumed that the appearance of lead ion vacancies plays the main role in the structural disordering. An increase of conductivity in DC and AC field, changes of current-voltage characteristics and AC- conductivity spectra are interpreted based on the model of hopping conductivity in disordered systems.
Photoinduced Effects in Single Crystals of PbO-MoO3 System
(Institute of Physics PAS, Poland, 2022) Bochkova, Tatiana; Bondar, Dmytro; Trubitsyn, Mykhailo P.; Volnianskii, M. D.; Volnyanskii, Dmytro M.
ENG: Purpose. Photoinduced changes in the optical absorption and dielectric properties of PbMoO4 and Pb2MoO5 crystals are considered. Differences in the manifestation of the photochromic effect in both crystals are associated with differences in their crystal structure. It is assumed that the photodielectric effect in the PbMoO4 and Pb2MoO5 crystals is due to the presence of the same anionic complexes. Methodology. Single crystals of PbMoO4 and Pb2MoO5 were grown in air from melt by the Czochralskii method. High-temperature treatment of the PbMoO4 crystals in air was carried out in a muffle furnace at 1200 K. The annealing time in the experiments varied from 2 to 90 h. Annealing of Pb2MoO5 crystals in vacuum was carried out at 1000 K during 1–2 h. The optical transmission spectra were measured at 295 K on the crystal doubly polished plates using a “Specord M-40” spectrophotometer. The photochromic coloration was observed after irradiation by light of Hg lamp during 2–5 h. Colored samples were returned to the initial state by annealing at 700–800 K in air for 2 h. Permittivity " was measured in the AC field by the four-wire method using a Keysight E4980AL LCR Meter at different frequencies (f = 1–10 kHz) in the temperature interval 290–700 K. Findings. One can assume that the photodielectric effect has the same nature and can be attributed for the common for both PbMoO4 and Pb2MoO5 crystals coordination complexes, i.e., molybdenum–oxygen tetrahedra. The dipole defects contributed to the photodielectric effect can be associated with Mo–O tetrahedra distorted by oxygen vacancy and photoelectrons capture. Hopping of VO through Mo–O tetrahedra vertices is accompanied by re-orientations of dipole moments of (MoO3)- complexes. Originality. Photoinduced changes in optical absorption and dielectric properties of PbMoO4 and Pb2MoO5 crystals are considered. The model of the mechanism of such changes of the power is offered. Practical value. The obtained conclusions will help to predict the influence of the composition of single crystals of acousto-optical materials of this series on their properties of practical value - optical absorption, optical stability..